    High-strength Insulation Ring

    Category Description: High-strength epoxy glass fiber insulation ring, made of high-strength alkali-free glass fiber filaments and heat-resisting resin by winding, △has high mechanical strength, corrosion resistance and dimensional accuracy, △is widely used for reversers and motor rotor starters, △a...
  • Category:
    High-strength Insulation Ring
  • Product number:
    q006
  • Release time:
    2021-08-23 15:32:16
  • INQUIRY

1.Data of Fiberglass Ring 

Properties

Unit

Typical

*Color
*Resin content ( weight % )
*Glass fiber content ( weight % )
*Composit density

*Circumferential tensile strength
at 20°C
(NOL test )

*Temperature at which the residual of
 Initial tensile strength is greater then
85%

*Fiber diretion thermal expansion coefficient (CTE)

*Thermomechanical analysis:
Glass transition temperature
(ASTM  E  1545-93 )

%
%
g/cm³

Mpa
(PSI)

 

°C
(°F)

 

1/K

 

°C
(°F)

Light brown
16-23
84-77
2.10-2.20

800-1200
(116000-174000)

 

300°C
(572°F)

 

8.50E-06

 

300-350°C
(572-662°F)

NOTE:

Mechanical NOL data vary within a range determined by resin content and the ratio diameted thickness of the ring .This ratio gives a flexural mode that will cocur during  test and test data can vary for each type of ring.

2.Data of Fiberglass Ring

 

Properties

Unit

Typical

*Color
*Resin content ( weight % )
*Glass fiber content ( weight % )
*Composit density

*Circumferential tensile strength
at 20°C
 (NOL test )

*Temperature at which the residual of
 Initial tensile strength is greater then
75%

*Fiber diretion thermal expansion coefficient (CTE)

*Thermomechanical analysis:
Glass transition temperature
(ASTM  E  1545-93 )

 

 

%
%
g/cm³

Mpa
(PSI)

 

 °C
(°F)

 

 1/K

 

°C
(°F)

 

 

 

Light brown
16-23
84-77
2.10-2.20

800-1200
(116000-174000)

 

200°C
(392°F)

 

8.50E-06

 

240-260°C
(464-500°F)

 

NOTE:

Mechanical NOL data vary within a range determined by resin content and the ratio diameted thickness of the ring .This ratio gives a flexural mode that will cocur during  test and test data can vary for each type of ring.

 